Abstract This paper aims at exploring the possibility of using a great percentage of recycled materials into vitreous china (VC), thus, contributing to urban waste decrease while lowering the industry’s buying costs, previously optimized, for the sanitaryware production. The recycled blend was introduced in the ceramic slip, Sanitser VC, and used in three sanitaryware production plants. This slip let to improve the environmental performances of the overall ceramic production through energy-saving and a decrease in greenhouse gas emissions. In fact, the firing temperature is 80-100 °C lower than traditional production. Therefore, the objective of this paper was to evaluate the firing behavior, technological properties, and microstructure of a typical industrial vitreous china body in comparison with Sanitser VC. The analytical results confirmed the force of this idea and highlighted the advantages of the choice made.

Resumo Neste artigo são apresentados os resultados do projeto europeu LIFE “Sanitser”. Este trabalho teve como objetivo reduzir a temperatura de queima da massa cerâmica (de 1250 para 1170 °C). Isto foi obtido substituindo a mistura de feldspato e quartzo por materiais reciclados e uma pequena percentagem de fundente (menos do que 3%); em uma formulação de massa de sanitário vitrificado foram introduzidos resíduos de vidro, granito e materiais cerâmicos quebrados após queima. Os testes realizados mostraram que a formulação Sanitser apresenta as mesmas propriedades físicas e químicas da cerâmica vitrificada (VC). Além disso, várias peças de cerâmica (lavatório, bidê e vaso sanitário) foram comparadas com a produção de VC. Os resultados mostraram que a massa Sanitser pode substituir a massa VC na produção industrial. Neste projeto a temperatura de queima do corpo cerâmico é significativamente reduzida com a suposta redução das emissões de CO2. Na formulação Sanitser foram utilizados cerca de 43,6% de materiais reciclados que acabariam em aterros sanitários.

Abstract In the present paper, the results of “Sanitser” Life European project are presented. The aim of this study was to reduce the firing temperature for ceramic body (from 1250 to 1170 °C). This was achieved substituting feldspar and quartz with recycled blend materials and a little percentage of flux (less than 3%); in a sanitary ware vitreous china formulation a waste glass, granitic materials and fired broken ceramic pieces were introduced. Tests performed on the Sanitser formulation showed that it has the same final physical-chemical characteristics of the industrial vitreous china (VC) body. Besides, different ceramic pieces (wash basin, bidet and WC pan) were compared with VC production. The results showed that Sanitser body can replace vitreous china in the sanitary ware production. In this project, the firing temperature of the ceramic body is reduced significantly with a supposed decrease of the CO2 emissions. In Sanitser formulation, about 43.6% of recycled materials that would end in dumps were utilized.

Polímeros redox vêm sendo amplamente empregados na preparação de eletrodos modificados em virtude de suas propriedades eletrocatalíticas. Este trabalho descreve a preparação e caracterização de eletrodos modificados de Pt e Pd, por eletrodeposição redutiva de trans-[RuCl2(vpy)4]. Os eletrodos preparados foram caracterizados por espectroscopia de impedância eletroquímica em diferentes potenciais dc. O circuito equivalente simulado para o eletrodo Pt/poli-trans-[RuCl2(vpy)4] em -186 mV dc é semelhante a um circuito R1(R2Q)C. Os diagramas de Nyquist não mostram diferenças significativas entre os eletrodos de Pt/poli-trans-[RuCl2(vpy)4] e Pd/poli-trans-[RuCl2(vpy)4]. Os gráficos obtidos para diferentes substratos, Pt e Pd, são semelhantes em formato, mas apresentam diferenças no valor de RΩ, sendo maior em Pd. Isto pode ser indicativo de maior queda ôhmica no sistema Pd/filme/solução. Os diagramas de impedâncias obtidos para o filme polimérico poli-{trans-[RuCl2(vpy)4]}, depositados sobre Pt ou Pd, variam de acordo com o potencial dc, em torno da onda voltamétrica do par redox Ru2+/3+. A inclinação da reta que representa a difusão de Warburg é maior no eletrodo de Pd, mostrando que nesse sistema ocorre um controle difusional maior.

Redox polymers has been highly employed in preparation of modified electrodes and yours electrocatalytic properties studied. This work describes the preparation of modified Pt and Pd electrodes by polymers by cathodic electrodeposition of trans-[RuCl2(vpy)4]. The electrodes were characterized by electrochemical impedance spectroscopy at different dc potentials. The equivalent circuit which simulated electrochemical impedance data obtained for the electrode Pt/poly-trans-[RuCl2(vpy)4] at -186 mV dc was R1(R2Q)C. From Nyquist plots, no significant differences between Pt/poly-trans-[RuCl2(vpy)4] and Pd/poly-trans-[RuCl2(vpy)4] electrodes could be observed. The plots corresponding to different substrates, Pt and Pd, show similar shape, but the RΩ value is higher in Pd electrode. Probably, this can be indication of ohmic fall higher in the Pd/film/solution system. The impedance plots obtained to the polymeric film trans-[RuCl2(vpy)4], deposited on Pt or Pd, vary with the dc potential closely the voltammetric wave of the Ru2+/3+ redox couple. The inclination of the plot corresponding the Warburg diffusion in the Pd electrode is higher than Pt electrode, showing a diffusional control.